This document describes two equivalent test methods for determining the glass content in Granulated blast furnace Slag (GBS) as constituent for common cement as defined on EN 197-1. Method A - Method of determining the glass content of GBS by X-ray diffraction. Method B - Method of determining the glass content of GBS by polarized optical microscopy. The glass content (or glassy/amorphous phase) in GBS is the fraction of the material that lacks a crystalline structure, having solidified rapidly from the melt in the form of amorphous glass. It is usually expressed as a percentage (wt%) of the total slag. In the absence of a product standard or a specification in the product standard, the constituent is tested at the fineness of the intended use. Furthermore, these test methods are used in manufacturing control of cement constituents for assessing their conformity to the limit indicated in EN 197-1.
Detta dokument föreslås att fastställas och publiceras som svensk standard.
För att lämna allmänna kommentarer på standardförslaget i sin helhet och på föreslagen titel – klicka på förslagets titel.
För att lämna specifika kommentarer på innehållet – skriv kommentaren och föreslagen ändring i rutan under avsnittet i fråga.
Standardförslag på engelska föreslås att fastställas som svensk standard utan översättning. Kommentarer på engelskspråkiga standardförslag bör vara på engelska.
För att ett standardförslag ska kunna fastställas som svensk standard måste det vara förenligt med svensk lagstiftning. Det är således viktigt att berörda svenska myndigheter klarlägger ifall standardförslaget är förenligt med svensk lagstiftning.