Nummer:ISO/DIS 6721-9
Källa:ISO
Kommitté:SIS/TK 156
Namn på kommittén:Plast
Publicerat:den 18 apr 2018
Sista svarsdatum:den 19 jun 2018
Ämnesområden:Plast: allmänt
Contact email:kommentera(at)sis.se
Förslagets omfattning:

This part of ISO 6721 describes a pulse propagation method for determining the storage component of the complex tensile modulus E' of polymers at discrete frequencies typically in the range 3 kHz to 10 kHz. The method is suitable for measuring materials with storage moduli in the range 0,01 GPa to 200 GPa and with loss factors below 0,1 at around 10 kHz. With materials having a higher loss, significant errors in velocity measurement are introduced through decay of amplitude.

The method allows measurements to be made on thin films or fine fibres and long specimens, typically tapes of 300 mm × 5 mm × 0,1 mm or fibres of 300 mm × 0,1 mm (diameter).

This method may not be suitable for cellular plastics, composite plastics and multilayer products.

Detta dokument föreslås att fastställas och publiceras som svensk standard.

För att lämna allmänna kommentarer på standardförslaget i sin helhet och på föreslagen titel – klicka på förslagets titel i innehållsförteckningen till vänster.

För att lämna specifika kommentarer på innehållet – skriv kommentaren och föreslagen ändring i rutan under avsnittet i fråga.

Standardförslag på engelska föreslås att fastställas som svensk standard utan översättning. Kommentarer på engelskspråkiga standardförslag bör vara på engelska.

För att ett standardförslag ska kunna fastställas som svensk standard måste det vara förenligt med svensk lagstiftning. Det är således viktigt att berörda svenska myndigheter klarlägger ifall standardförslaget är förenligt med svensk lagstiftning.